Equivalent grades |
GB |
DIN |
AISI |
JIS |
DAIDO |
3Cr2MnNiMo |
1.2738 |
P20+Ni |
-- |
-- |
Chemical Composition |
C |
Si |
Mn |
Cr |
P |
S |
Ni |
Mo |
W |
Other |
0.35-0.48 |
0.20-0.40 |
1.30-1.60 |
1.80-2.10 |
0.03MAX |
0.03MAX |
0.90-1.20 |
0.15-0.25 |
- |
- |
Available size |
Round Bar |
Diameter |
Length |
60-800mm |
2000-6000mm |
Flat Bar |
Thickness |
Width |
Length |
25-400mm |
200-800mm |
2000-6000mm |
Surface condition |
Black surface/ Grinded/ Machined |
Annealed hardness |
28-35 HCR (After tempering ) |
Characteristics |
Good polishing and photo-etching properties Good machinability High purity and good homogeneity Uniform hardness |
Applications |
Injection moulds for thermoplastics |
Extrusion dies for thermoplastics |
Blow moulds |
Forming tools, press – brake dies (possibly flame hardened or nitrided ) |
Aluminium die casting prototype dies |
Structural components, shafts . |
Heat Treatment |
Annealing
|
710 - 730 °C |
Hardness after annealing
|
Max. 240 HB |
Stress relieving
|
Approx. 600 °C |
Hot forming
|
1050 - 850 °C |
Hardening
|
870 - 890 °C |
Quenching media
|
Oil, Salt bath, Vacuum |
Hardness after quenching
|
50 - 54 HRC |
Hardness after tempering
|
100 °C |
200 °C |
300 °C |
400°C |
52HRC |
51HRC |
49HRC |
46HRC |
|
|
|
|
|
|
|
|
|
|
|